Remora Heatshrink end caps are manufactured from cross-linked polyolefin material and are coated with a hot melt adhesive on the inner surface. This provides a water tight seal against the damage of moisture, dirt or corrosion. The rugged wall of these end caps also offers excellent resistance against abrasion. Suitable for use on polymeric and paper insulated, lead jacketed cables.
• Good chemical resistance
• Good solvent resistance
• Unaffected by UV light
• 2:1 Shrink Ratio
• Zero Halogen
Dielectric Strength: 12 kV/mm min
Temperature Range -55°C to 100°C
Shrink Temperature: +120°C
Tensile Strength: 12.0 MPa min
Tensile Strength After Heat Ageing: 68 hours @ 120°C - 10 MP a min
Elongation: 300% min
Elongation After Heat Ageing: 168 hours @ 120°C - 250% min
Material: Cross-linked Polyolefin. Internally coated with Hot Melt Adhesive
Colour: Black